    High Manganese Steel DIN 1.3401

    Sheffield 14% Manganese is a true Hadfield Austenitic Manganese steel for resistance to severe impact and abrasive wear. This product will work harden in service up to 550 BHN. Because this product hardens under cold work conditions care should be taken when forming, drilling or machining is being considered.

    Sheffield 14% Manganese can be welded with standard manganese electrodes. Please use only certified personnel who are familiar working with this type of material. Drilling is not recommended for this product.

    Manganese is gray-white metal with a pinkish tinge, and a very brittle but hard metallic element. Manganese is a reactive element that easily combines with water and air. It is a steel with a relatively large component about 10-14% of manganese; highly resistant to wear and shock.

    The original austentic manganese steel, containing about 1.2%C and 12% Mn.

    MANGANESE ADVANTAGES

    WORK HARDENING refers to the fact that the steel becomes harder and harder the more it is impacted or compressed.

    The “Hadfield” grade has an original hardness of approximately 220 BRINELL. With continued impact and /or compression it will surface harden to over 550 BRINELL.

    It should be noted that only the outer skin surface hardens. The under layer remains highly ductile and tough. As the surface wears, it continually renews itself becoming harder and harder.

    Manganese steel is an austenitic steel which means it is non-magnetic. This property makes it useful in many applications such as bottom plates for lifting magnets – separator drum shells for magnetic materials – wear shoes on electric brakes etc.



    Advantages

    Resistance to high abrasion and severe impact.
    • Will work hardened rapidly to 550BHN.
    • Remains ductile throughout.
    • Hadfield Grade.
    • Can be welded.
    • Has non-magnetic properties.
    • Can be cut with oxy-acetylene torch, plasma, water jet, or laser.
    • Made to the toughest standards in the industry for extended service life.

    Applications

    • Wheelabrators

    • Shake-Out Decks

    • Shot Blast Cabinets

    • Sintering Seal Bars

    • Scrappers

    • Screens

    • Crusher Liners

    • Grader Blades

    • Elevator Buckets

    • Baffle Plates

    • Stone Chutes

    • Bucket Liners

    • Crusher Jaws

    • Hammers

    • Chain Wear Bars

    • Grizzly Bars


    CHEMICAL COMPOSITION (TYPICAL)


    C (%)

    Mn (%)

    Si (%)

    S (%)

    P (%)

    ASTM 128 Gr B2

    1.05 – 1.2

    11.5 – 14

    < 1.0

    <0.070



    MECHANICAL CHARACTERISTICS

    YIELD

    TENSILE UTS 20° C (68° F)

    ELONGATION

    CHARPY Kcvl 20°C (4°F)

    HARDNESS BHN

    350 MPa

    51 KSI

    940 MPa

    136 KSI

    (5d)

    40%

    >140J/cm2

    100 ft. lbs

    220 to

    540


    EQUIVALENT STANDARDS:


    STANDRADS


    EURONORM

    DIN

    ASTM

    AFNOR

    GRADES

    X120Mn13

    1.3401

    A128 GR B2

    A128M

    X120Mn13

    2,56,870

    STANDRADS


    IS:2000

    IS:1993

    BS

    GRADES

    276

    2708

    3100

     

    Trade Information
    • Cheque
    • 1000 KG Per Day
    • 3-4 Week
    • Yes
    • Sample costs shipping and taxes has to be paid by the buyer
    • Africa, Middle East, Western Europe, Eastern Europe, South America, North America, Central America, Australia, Asia
    • All India
    Contact Us

    Shreepati Castel , 10/11 1st Floor, Wing D-1 11 Khetwadi, Mumbai, Maharashtra, 400004, India
    Phone :91-22-23894572/67496094/67496097